size
25.2 mm x 35.6 mm x 1.1 mm
substrate.thickness
1.05 mm
substrate.type
low-autofluorescence optical quality glass
ravg-and-passband-range.1
Ravg > 95% 350 – 404 nm
tavg-and-passband-range.1
Tavg (see below) 414 – 450 nm
ravg-and-passband-range.2
Ravg > 95% 461 – 487.5 nm
tavg-and-passband-range.2
Tavg (see below) 499.5 – 530 nm
ravg-and-passband-range.3
Ravg > 95% 543 – 566 nm
tavg-and-passband-range.3
Tavg (see below) 580 – 611 nm
ravg-and-passband-range.4
Ravg > 95% 626 – 644 nm
tavg-and-passband-range.4
Tavg (see below) 659.5 – 850 nm
Optical.Damage.Rating
Testing has proven to show no signs of degradation when exposed to at least 6.0 W of power from an unfiltered xenon arc lamp over a 25 mm diameter (corresponding to 1.2 W/cm2) for over 500 hrs.
Transverse.Dimensions.(LxW)
25.2 mm x 35.6 mm
Transverse.Tolerance.(mounted)
± 0.1 mm
Filter.Thickness.(unmounted)
1.05 mm
Filter.Thickness.Tolerance.(unmounted)
± 0.05 mm
Clear.Aperture
≥ 80% (elliptical)
Orientation
Reflective surface marked with part number - Orient in direction of incoming light
RWE.1
>> 6λ P-V RWE @ 632.8 nm
aoi
Tavg > 93% 414 – 450 nm
aoi
Tavg > 90% 414 – 450 nm (AOI = 45° ± 1.5°)
aoi
Tavg > 93% 499.5 – 530 nm
aoi
Tavg > 90% 499.5 – 530 nm (AOI = 45° ± 1.5°)
tavg-and-passband-range.3
Tavg > 93% 580 – 611 nm
tavg-and-passband-range.3
Tavg > 90% 580 – 611 nm (AOI = 45° ± 1.5°)
tavg-and-passband-range.4
Tavg > 93% 659.5 – 850 nm
tavg-and-passband-range.4
Tavg > 90% 659.5 – 850 nm (AOI = 45° ± 1.5°)